Recently, due to increase in the usage of toxic gas and inflammability gas, the ability to monitor and precisely measurement of these gases is crucial in preventing the occurrence of various accidents. CuO doped and undoped $WO_3$ thick films gas sensors were prepared using screen-printing method on alumina substrates. A structural properties of $WO_3$:CuO thick films had monoclinic phase and triclinic phase of $WO_3$ together. Sensitivity of $WO_3$:CuO sensor at 2000 ppm of $CO_2$ gas and 50 ppm of $H_2S$ gas was investigated. 4 wt% Cu doped $WO_3$ thick films had the highest sensitivity of $CO_2$ gas and $H_2S$ gas.