The purpose of this study is to provide basic data for utilization in environment-friendly and economically outstanding CSG construction method by physical and mechanical properties of CSG materials including characteristics of uniaxial compressive strength, microscopic structure and freezing and thawing resistance in accordance with the cement content and curing time of the cement, and size of specimen. In this study, specimens with cement content of 4, 6, 8 and 10% of the total weight were, and, in order to examine the characteristics of the sizes of specimen, specimens with ${Phi}50{ imes}100mm$, ${Phi}100{ imes}200mm$ and ${Phi}150{ imes}300mm$ were manufactured to assess the features including compressive strength, microscopic structure, freezing and thawing, and degree of wet-dry. As results, it was found that with greater size specimen or contents of cement in the specimen, compressive strength, freezing and thawing resistance, and wet-dry resistance increase. Moreover, reactive products for each size of specimen were examined and it was possible to verify that some typical needle structured ettringite was generated due to blending of cement through microscopic structure analysis such as SEM and EDS analysis.