Hydriding combustion synthesis (HCS) can produce full hydrides of alloys and in a short time. The conventional process based on ingot metallurgy cannot produce Mg-based alloy easily with the desired composition and the cast product needs a ling activation process for the practical use of hydrogen storage. In this study, the hydriding properties of Mg-xNi (x=5, 13.5, 54.7wt.%) alloys prepared by hydriding combustion synthesis were evaluated. The hydrogen storage capacity and kinetics of HCS Mg-xNi alloys were strongly dependent on the content of Ni. The HCS Mg-13.5wt.%Ni alloy shows the hydriding behavior to reach the maximum capacity within 30 min. and the reversible $H_2$ storage of 5.3wt.% at 623 K.