Nylon 6 was blended with a brominated epoxy resin, tetrabromobisphenol A diglycidyl ether (DGEBBA), to enhance flame retardant property. Thermal properties of the blends were analyzed by DSC. Melting point and crystallization temperature decreased as the amount of epoxy resin increased. Melt index and relative viscosity decreased as the amount of the epoxy resin increased. When the blended amount of the epoxy resin was below 5%, the melt index decreased while the relative viscosity slightly increased. The blend resin was successfully spun into fiber without swelling or drawing the resonance phenomena. However, both the tenacity and elongation of the fiber decreased by increasing the amount of the DGEBBA.