For the purpose of evaluating to remove elemental mercury using SCR (Selective Catalytic Reduction) catalysts, the result of the concentration variation of elemental mercury in lab experiment and field measurement was compared. The effect of the elemental mercury oxidation on commercial catalysts was studied in simulated gas. Three species of SCR catalyst, $V_2O_5-TiO_2$ type, were selected. The elemental mercury reduced 30% without HCl gas in SCR operating condition. But the width of reduction increased 60% at 20 ppm HCl gas. According to the result of field measurement, reduction rate of elemental mercury at SCR outlet showed 60%. The total mercury concentration decreased about 20%. The results were similar to the lab test. The results of chemical analysis of test sample showed increase of mercury concentration but surface change was not observed.