In this research, an effective method for reducing the fibrillation of lyocell fibers, which are spun from a solution of cellulose in N-methyl morpholine-N-oxide(NMMO), through consecutive chemical treatments. Undried solution-spun cellulosic fiber was firstly treated with 10 to 30 wt% of multifunctional crosslinking agents, such as ethylene glycol poly(3-chloro-2-hydroxypropyl) ether, and then dipped into alkaline solution to introduce epoxy functions. Finally steam condition was applied to occur a chemical crosslinking in order to reduce the fibrillation on the surface of fibers. Fibrillation was also reduced significantly by adding extra $Na_2SO_4$ in NaOH solution. In addition, Antifibrilllated lyocell fibers show the slightly higher dyeability(4 %) to Cibacron Blue without serious reduction of mechanical properties.