$Y_{1-x}PO_4:{Eu_x}^{3+}$ red phosphors were synthesized with changing the concentration of $Eu^{3+}$ ion by using a solid-state reaction method. The crystal structures of all the red phosphors were found to be a tetragonal system composed of (200) diffraction peak centered at $25.88^{circ}$, and the morphology of grains approached the spherical form with homeogenous size distribution as the concentration of $Eu^{3+}$ ion increased. As for the photoluminescence properties, all of the ceramic phosphors, irrespective of $Eu^{3+}$ ion concentration, showed the red-orange and the red emission peaked at 593.0 and 619.2 nm respectively. As the concentration of $Eu^{3+}$ ion increased, the excitation spectrum moved into a longer wavelength with the increase of emission intensity. The maximum excitation and the emission spectrum were observed at 0.15 mol of $Eu^{3+}$ ion.