The sintering behavior and microwave properties of ferrite ($Ba_3Co_{2-2x}Zn_{2x}Fe_{24}O_{41}$ ceramics) were investigated for microwave applications. Also PIFA type antenna with ferrite was simulated. All samples were prepared by the solid state reaction method and sintered at $1350^{circ}C$. All ceramics had relatively density above of 92% compare with theoretical density of $Ba_3Co_2Fe_{24}O_{41}$ ceramics. From the XRD pattens, the Z-type phase was existed as main phase in $Ba_3Co_{2-2x}Zn_{2x}Fe_{24}O_{41}$ ceramics. The permittivity and permeability of $Ba_3Co_{2-2x}Zn_{2x}Fe_{24}O_{41}$ ceramics were increased with Zn additions and decreased rapidly over frequency of 200~600 MHz. Several PIFA type antennas with ferrite and FR4 were simulated. All antenna structure had return loss of less than -10 dB at each resonant frequency. Simulated antenna using both ferrite and FR4 showed size reduction of 25% without a significant decrement of efficiency.