We investigated the low firing of $Li_2CO_3$ added $0.2Pb(Mg_{1/3}Nb_{2/3})O_3$ - 0.3Pb($Fe_{1/2}Nb_{1/2}$) - $0.5Pb(Zr_{0.475}Ti_{0.525})O_3$ (PMN-PFN-PZT) ceramics and multilayer actuators (MLAs) using Ag inner electrodes. It was found that 0.1 wt% $Li_2CO_3$ was quite effective in lowering the sintering temperature of PMN-PFN-PZT ceramics from $1,100^{circ}C$ down to $900^{circ}C$ without deteriorating their piezoelectric ceramics ($d_{33}$ = 425 pC/N and $k_p$ = 61.9%). However, excess $Li_2CO_3$ up to 0.3 wt% brings about unwanted problems such as the formation of a $LiPbO_2$ secondary phase and subsequent degradation in the piezoelectric properties. Using 0.1 wt% $Li_2CO_3$ added PMN-PFN-PZT ceramics, MLAs with Ag inner electrodes were successfully fabricated, resulting in a normalized strain of 580 pm/V at an electric field of 1.5 kV/mm.