Nano-technology is a super microscopic technology to deal with structures of 100 nm or smaller. This technology also involves the developing of $TiO_2$ materials or $TiO_2$ devices within that size. The aim of the present paper is to synthesize $WO_x$ doped nano-$TiO_2$ by the Sonochemistry method and to evaluate the effect of different percentages (0.5-5 wt%) of tungsten oxide load on $TiO_2$ in methylene blue (MB) elimination. The samples were characterized using such different techniques as X-ray diffraction (XRD), TEM, SEM, and UV-VIS absorption spectra. The photo-catalytic activity of tungsten oxide doped $TiO_2$ was evaluated through the elimination of methylene blue using UV-irradiation (315-400nm). The best result was found with 5 wt% $WO_x$ doped $TiO_2$. It has been confirmed that $WO_x-TiO_2$ could be excited by visible light (E<3.2 eV) and that the recombination rate of electrons/holes in $WO_x-TiO_2$ declined due to the existence of $WO_x$ doped in $TiO_2$.