Effects on sintering and electrical properties of $La_{0.7}Ca_{0.3}Cr_{0.9}Co_{0.1}O_{3-{delta}}$ system, a interconnect material for cylindrical and flat tubular solid oxide fuel cells (SOFC), have been investigated by Ca-source when using $CaCO_3$ and $CaF_2$. When using $CaCO_3$ and $CaF_2$ was mixing as Ca-source, single phased perovskite solid solution was observed for each sample. The sintering temperature was decreased by $CaF_2$ contents was increased. When using 0.1 mole $CaF_2$ was densely sintered at $1400^{circ}C$ and relative density was 93.8%. Also, electrical conductivity in oxidation and reducing atmosphere was 47, 4.3 S/cm, respectively, due to $F^-$ ion enhance the electrical conductivity in reducing atmosphere.