In this work, the adsorption characteristic of the composites by adding loess with aluminum ("Al-loess") and Loess with lanthanum ("La-loess") which have been developed to effectively remove phosphorus, the substance which causes the eutrophic lake has been evaluated. According to the result of the work, as the amount of aluminum or lanthanum put in 1g of loess increases, the combined amount also increases accordingly. When the loess with no aluminum or lanthanum attached was used, the rate of removing phosphorus was different in comparison with the case of using the composites of 0.5, 1 and 2 mg of aluminum and 0.5, 1 and 3 mg of lanthanum in each gram of loess. It was observed the amount required to remove 1 mg $PO_4^{3-}$-P/L of phosphorus completely is approximately 2 to 10 times less for the composite of Al-loess than loess alone. Also, in case of the composite of La-loess, the amount was decreased by about 1.5 to 10 times. In order to observe the rate of adsorption phosphorus with Al-loess and La-loess, the composites were used for the observation up to three times by water washing. As a result, the water washing of the composite did not affect phosphorus removal. According to the effect of pH, there is a high rate of removing phosphorus in the pH range of 5~8. It seems that the developed composite will effectively remove phosphorus when it is spread in the natural water system. Also, since Al-loess and La-loess composites are rapidly precipitated within 30 minutes, it is stabilized quickly at the bottom of the eutrophic lake and becomes responsible for the removal of phosphorus in water and eluted from the water and the sedimentary layer.