In order to make a $Cu_2ZnSnSe_4$ (CZTSe) sputtering target sintered for solar cell application, synthesis of CZTSe compound by solid state reaction of Cu, Zn, Sn and Se mixed powders and effects of ball milling condition on sinterability such as ball size, combination of ball size, ball milling time and sintering temperature, was investigated. As a result of this research, sintering at $500^{circ}C$ after ball milling using mixed balls of 1 mm and 3 mm for 72 hours was the optimum condition to synthesis near stoichiometric composition of $Cu_2ZnSnSe_4$ and to prepare sintered pellet with high density relatively.