Using a mechano-luminescent(ML) paint, which allows the visualization of fast propagating crack under conventional loading conditions, a catastrophic fracture mechanism associated to crack tip melting and wake bridging in bulk metallic glass, is described in this paper. Fracture occurs in two steps with, first, crack initiation from the mechanically machined sharp notch tip in a rectangular shaped compact tension specimen and melting of its tip due to intense shear deformation within very few deformation bands. Then, the crystalline phase in the glass matrix gradually converts the molten crack into a conventional bridged crack as it propagates.