In this study, lead-free $(Na_{0.5}K_{0.5})NbO_3-BiTiO_3$ ceramics were fabricated by a conventional mixed oxide method. Structural and electrical properties of lead-free $(Na_{0.5}K_{0.5})NbO_3$ ceramics with the variation of $BiTiO_3$ were investigated. The results of X-ray diffraction analysis showed a typical polycrystalline perovskite structure without presence of the second phase in all specimens. Sintered density increased with an increasing of BTO and the specimen added with 0.07 mol% of $BiTiO_3$ showed the maximum value of 97.8%. Average grain size decreased and densification increased with an increasing of $BiTiO_3$ contents. The electromechanical coupling factor of the 0.01 mol% $BiTiO_3$ doped NKN specimens was 0.32. Dielectric constant, dielectric loss and Curie temperature of the 0.07 mol% $BiTiO_3$ doped NKN specimens were 1185, 0.145% and $400^{circ}C$, respectively.