Purpose: This study was conducted to identify the surface characteristics of titanium discs coated with MS275/PLGA by electrospray and which is effective to mesenchymal stem cell proliferation. Materials and methods: We used anodized surface coated with PLGA as a control group and anodized surface coated with MS275 $0.5{mu}M$, $1{mu}M$, $1.5{mu}M$ as test groups. To examine that the coating particles are nanometer sized, FE-SEM was used and AFM was utilized to determine the difference of coating surface roughness. We checked the mesenchymal stem cell proliferation by using MTT assay on $1^{st}$, $4^{th}$, $7^{th}$ days. Results: There was no significant difference between control groups and test groups in AFM results (P>.05). In MTT assay results, mesenchymal stem cell proliferation was increased with time, at $7^{th}$ day, cell viability on discs coated with $1.5{mu}M$ MS275 was significantly higher than control group (P<.05). As SEM showed, the number of cells on all discs was increased and the morphology of cell attachment was also wider and closer with time. Conclusion: Titanium surface coated with MS275/PLGA showed significantly higher cell proliferation and the more density of MS275 was dispersed on titanium discs, the faster cells grew.