To examine the deformation characteristics of round aluminum pipe under biaxial compression, a horizontal biaxial compression die was fabricated. The change of material properties, punch load and deformation behavior were monitored in experiments using various compressive deformation rates in the range of 1mm/min.~400mm/min. The tensile and compressive strains were estimated from Vickers microhardness results. The punch load and deformation characteristic of the round aluminum pipes were found to change greatly at a deformation rate of about 200mm/min. The punch load decreased with increasing compressive deformation rate. Results of numerical simulation using Deform-2D were in good agreement with experimental results, and the measured hardness variation with the strain variation was predicted well by the simulation.