In this study, some experimental results of the peroxide-degradation process of polypropylene(PP) in a co-rotating twin-screw extruder to produce controlled rheology polypropylene(CRPP) are presented. The peroxide was dicumyl peroxide(DCP) and the concentration of DCP was in the range 0-0.3 wt%. It was found that the rheological properties of PP change significantly during reactive extrusion. Melt flow index(MFI) increased with DCP concentration. Intrinsic viscosity decreases with increasing DCP concentration. From dynamic rheological data, number average molecular weight(Mn), weight average molecular weight(Mn) and molecular weight distribution(MWD) were calculated. Results indicated that Mw decreases and MWD becomes narrower with increasing peroxide concentration. Especially, particle size distribution of CRPP decreases with increasing DCP concentration by chemical powdering process, and anti-slip floor paint, CRPP(DCP 0.2 wt%) powder by 10phr was friction coefficient 2.15 ${mu}$, abrasion resistance 511.18%.