Polyester is mainly used as a bedding filler material. PLA fiber as an eco-friendly material for substituting polyester has a low melting temperature and therefore a hardening process is impossible. This study is to develop the oil for feather touch that can treat at the melting temperature of PLA. The slippery and soft aminosilicone emulsion, and the bulky epoxysilicone emulsion were used. They had proper viscosity and particle size for flexibility and elasticity. When using methoxy aminosilane [$H_2NSi(OCH_3)_3$] as an aminosilane and [$Zn(OCOCH_3)_2$] as a catalyst, the hardening reaction was fast and effective. Feather touch process were treated by 2 steps. At first step, aminosilicone emulsion, epoxysilicone emulsion and methylaminosilane were mixed and homogenized, and at second step, 5% blened solution of the first step, Zn catalyst 1%, distilled water 94% were treated at PLA fiber. After treatment the static friction coefficient and dynamic friction coefficient were reduced to 23.5-60.8% and 30.0-61.3% respectively, and the laundry and sun light fastnesses have not shown any decrease.