In this study, the current-voltage curves for metals were measured using cyclic voltammetry. The relationship between the electrochemical properties and surface states of metals were investigated by Scanning Electron Microscope (SEM). In cyclic voltammetry, we used a 3-electrode system for the electrochemical measurements. The measurement was conducted at the condition that consists of the first reduction from the initial potential to -1350 mV, continuous oxidation to 1650 mV, and last reduction to the initial potential. The scan rates were 50, 100, 150 and 250 mV/s. The results show the C-V characteristics of metals to be for an irreversible process, which was caused by the oxidation current from cyclic voltammogram, when monoethanolamine (MEA) was used as a corrosion inhibitor. When we used MEA as a corrosion inhibitor, the diffusion coefficient was decreased as the concentration of electrolyte was increased. In the SEM images of copper, we observed an increase of surface corrosion at the increased electrolyte concentration. Addition of $1.0{ imes}10^{-3}M$ corrosion inhibitor MEA reduced the effect of corrosion prevention due to the relatively large diffusion coefficient at the electrolyte concentration of 0.1N.