A vacuum ladling die casting system is suggested as a means to obtain a high vacuum level. A high vacuum of 17.8 mmHg is obtained by sealing the inner space of the mould. The sample product is a rear-head housing for an auto-compressor, and the die-casting with 6-cavities was conducted. The flow analysis shows that the filling speed during vacuum ladling is faster than for a non-vacuum system. The air holes in the sample product were too small to be seen with the naked eye in X-ray films. Density tests show that the high vacuum ladling system reduces the internal porosity as much as 57.8% when compared to the non-vacuum system. A defective rate of only 0.17% was found from leak testing. The results of this research prove that the high vacuum die-casting process is useful for manufacturing of aluminium components under high internal pressure.