A series of novel polytriazoleimides were prepared from various aromatic dianhydrides and a new kind of 1,2,3-triazole-containing aromatic diamine synthesized by the Cu (I)-catalyzed 1,3-dipolar cycloaddition reaction in DMAc, and characterized by FT-IR, $^1H$-NMR, XRD, DSC and TGA techniques. The results show the polytriazoleimides are soluble in most of strong polar solvents and have inherent viscosity values of 0.51-0.62 dL/g(DMAc). The polytriazoleimide films exhibit a tensile strength of 62.3-104.5 MPa and an elongation at breakage of 4.0-8.1%, a glass transition temperature ($T_g$) of $257-275^{circ}C$, a decomposition temperature (at 5% weight loss) of $350-401^{circ}C$ in $N_2$ atmosphere, and a dielectric constant of 2.47-3.01 at 10 MHz, which depend on the structure of the polymers. The polytriazoleimides perform good resistance to acid and alkali solution.