The optimum dewaxing ratio in dewaxing treatment by the heat and pressure method was investigated by considering aging stability of dewaxed Hanji. Commercial Hanji was coated with beeswax and thermally aged at $150^{circ}C$ for 24 hours. Then it was dewaxed using the laboratory sheet press equipped with hot plates on both top and bottom sides. Dewaxing ratio was controlled by pressing temperature and time. Four type of dewaxed Hanji samples with different dewaxing ratio were prepared and thermally aged at $150^{circ}C$. Then the aging stability of dewaxed Hanji samples was evaluated in terms of optical and strength properties. It was found that the aging stability of dewaxed Hanji was superior with higher dewaxing ratio. The result concluded that, in the aspect of aging stability, the coated beeswax in beeswax-treated Hanji shall be completely removed if the coated wax would be dewaxed.