In this study, lead-free $(Na_{0.465}K_{0.465}Bi_{0.07})(Nb_{0.93}Ti_{0.07})O_3-0.08MnO_2$ ceramics were fabricated by conventional mixed oxide method. Structural and electrical properties of lead-free $(Na_{0.465}K_{0.465}Bi_{0.07})(Nb_{0.93}Ti_{0.07})O_3-0.08MnO_2$ ceramics with the variation of sintering temperature were investigated. As results of x-ray diffraction analysis, all specimens showed a typical polycrystalline perovskite structure without presence of the second phase. Sintered density increased with an increases of sintering temperature and the specimen sintered at $1,020^{circ}C$ showed the maximum value of 4.5 $g/cm^3$. The average grain size of the $(Na_{0.465}K_{0.465}Bi_{0.07})(Nb_{0.93}Ti_{0.07})O_3-0.08MnO_2$ specimen sintered at $1,020^{circ}C$ is about 0.83 ${mu}m$. Electromechanical coupling factor, relative dielectric constant and dielectric loss of $(Na_{0.465}K_{0.465}Bi_{0.07})(Nb_{0.93}Ti_{0.07})O_3-0.08MnO_2$ specimens sintered at $1,020^{circ}C$ were 0.252, 741 and 0.043% respectively.