Precast concrete method is known to have advantages of minimizing works in the construction, controlling concrete quality easily and saving construction period due to only fabrication work in the construction field, but it needs to apply steam curing to accelerate early concrete strength. In the meanwhile, the oil cost for steam curing has been continuously increased because of political instability in the middle East and international economic shaky. Thus, this study addresses the development of precast/ prestressed concrete which has over 14MPa at 1 day age and specified concrete strength of 40MPa at low temperature, not applying steam curing. Tests were carried out in terms of material characteristics in fresh concrete and compressive strength using 3 types of cement such as Type I, Type III and rapid hardening compound cement. As results of tests, it is found that cements for rapid hardening had disadvantages with respect to slump, slump loss, and air content, but showed higher compressive strength than specified one, especially the highest value when using rapid hardening compound.