Objectives : The aim of this investigation was to evaluate the remineralization effect of Bamboo salt and NaF+Bamboo salt solutions on bovine enamel formed incipient artificial enamel caries by microcomputed tomography (micro CT). Methods : Experimental solutions were distilled water(negative control), 2% sodium fluoride solution (2% NaF group), 3% bamboo salt solution (3% BS group) and the solution mixed 2% sodium fluoride solution and 3% bamboo salt solution (2% NaF+3% BS group). Specimens were prepared from extracted bovine teeth and divided into 4 groups of 10 specimens each by randomized blocks according to density. Then the specimens surface were divided equally into three parts to observe sound enamel area, incipient enamel carious area and remineralized enamel area. Only one-third of specimen surface was coated with nail varnish and these were exposed to a lactate carbopol buffer system for 72 hours. Then one-half of the demineralized enamel area was coated with nail varnish. The specimens were carried out under pH cycling model for 14 days as follows; samples were immersed in each experimental solution for 2 mins 3 times per day, demineralized for 4 hours and in mixed saliva for the remaining hours. After pH cycling, density was measured using micro CT. Results : All experimental groups showed remineralization effects except for negative control group(p<0.05). The differences of density after experimental solution treatment were statistically significant difference among 4 groups (p<0.01). The density difference values of groups were $0.04{pm}0.01$ in negative control group, $0.19{pm}0.01$ in 2% NaF group, $0.14{pm}0.01$ in 3% BS group, and $0.21{pm}0.01$ in 2% NaF+3% BS group. Conclusions : The bamboo salt solution showed remineralization effects on incipient artificial enamel caries and the solution mixed sodium fluoride solution and bamboo salt solution showed more remineralization effects than the bamboo salt solution. Thus, it is suggested that bamboo salt can be used as remineralization agent in incipient enamel caries lesion.