The aim of this study is to investigate mechanical and fracture behavior of plane weave glass fiber reinforced high density polyethylene (HDPE) thermoplastic composite using a middle tension (MT) specimen with inclined through-thickness cracks under static tension. In this study, crack growth, crack opening displacement (COD), stress intensity factors and fracture toughness are studied. Crack growth and crack opening displacement values are taken as a damage parameter factor for crack geometry calculations. Experimental results are evaluates using both J-integraland stress intensity factormethods.