Polyacrylate dispersion(emulsion) as adhesive material was superior in quality such as preservation characteristics and reversibility. The tapes for repairing archival documents manufactured with four different types of formulation resulted in pH 7~8.8, soluble solid 50~52%, and viscosity 1,300~2,500 cps. Sample 4 of those was most excellent. Probably, sample 4 included inorganic materials such as MgO, silica gel, and zeolite. For selecting carrier of tape, tracing papers, were applied for manufacturing tapes and tested for adhesive strength and peel strength. Adhesive strength of tracing papers, was 3.1~3.8(N/10mm), 2.2~2.8(N/10mm), and 1.7-2.3(N/10mm), respectively. Peel strength was similar in all samples. To determine characteristic of conservation to the selected carriers, stability of deterioration was examined at conditions of $105^{circ}C$ and $80^{circ}C$ 65% for 7 days.