Glasses were prepared with compositions of $(13-x)BaO-80B2_O_3-7Li_2O{cdot}xSm_2O_3$, BBLSx(x=0.5, 0.4, 0.3) by melting the starting materials of boron oxide(99.9%), lithium oxide(99.9%), barium carbon oxide(99.9%), and samarium oxide(99.9%) and then quenching the melt at $1350^{circ}C$. This led to good-quality BBLSx(x=0.4, 0.3) and poor-quality BBLSx(x=0.5) glasses. The physical and structural properties of the BBLSx glasses were studied by means x-ray diffraction, scanning electron microscopy(SEM), differential scanning calorimetry(DSC), and dielectric spectroscopy. From the x-ray diffraction and SEM results, the quality of the BBLSx glasses significantly depends on the $Sm_2O_3$ concentration. The x-ray diffraction pattern showed that the crystallites in the BBLSx glasses after heat treatment at $700^{circ}C$ may be $LiBaB_9O_{15}$. From the DSC results, the glass transition temperatures($T_g$), crystallization temperatures($T_c$), and the maximum temperatures of the crystallized($T_p$) BBLSx glasses all changed with the $Sm_2O_3$ concentration. According to the dielectric spectroscopy results, the values of the real dielectric constant and Tan ${delta}$ of the BBLSx glasses depended on the $Sm_2O_3$ concentration. The values of the real dielectric constant and Tan ${delta}$ were also shown to depend on the measuring temperature, possibly due to the ion migration in the bulk of the BBLSx glasses.