In this study, MMT/fiber/polymer composites were fabricated by impregnating chopped strand glass mat into a vinylester resin mixed with clay. Tensile tests has been performed by using a universal testing machine to determine the effect of MMT addition on the tensile properties of MMT/chopped strand glass fiber/vinylester composites. And some pictures which are magnified cross section of breaking parts are has been taken by using a FE-SEM to confirm the behavior at breaking. The contents ratio of MMT applied in the composites were 0.5, 1.0, 1.5, and 2.0 wt% respectively. It has been found that the tensile strength and elastic modulus of MMT/chopped strand glass fiber/vinylester composites were improved at a proper content of MMT. Tensile strength and elastic modulus were maximized at a content of 1.0 wt% due to most effective dispersion of MMT. On the contrary, the failure strain was increased as MMT content was increased.