A temperature dependent (10K-290K) photoluminescence (PL) study for two differently prepared ZnO thin films (as-grown and O-plasma treated) is presented. Four characteristic peaks were identified for both samples: (i) neutral donor-bound excitons ($D^oX$), (ii) two electron satellites (TES), (iii) phonon replica of $D^oX$ ($D^oX$-1LO), and (iv) donor-acceptor pair transition (DAP). As the sample temperature increased, $D^oX$-1LO and DAP transitions became indistinct. This was accompanied by newly-rising emission of free electron-acceptor transitions (e, $A^o$). The spectral evolution with temperature for as-grown samples also showed the optical emission from free excitons, which became dominant at higher temperatures. Some features related to O-plasma were identified in PL spectra: (i) different positions of TES transitions (28meV lower than $D^oX$ for as-grown samples and 35meV for O-plasma treated samples), (ii) the decrease of spectral intensity in both emissions of $D^oX$ and DAP after O-plasma treatment, and (iii) no noticeable transition from free excitons after the O-plasma treatment.