본 연구에서는 LNG저장시설용 수화열 저감형 콘크리트 적용을 위하여 최적의 결합재를 개발하고자 하였다. 결합재는 1종포틀랜드시멘트, 고로슬래그미분말, 플라이애시를 혼합 사용하였다. 또한 여기에 미립자시멘트 및 자극제를 첨가하여 조강성능 향상 및 석회석 고미분말을 사용하여 경제성을 향상시켰다. 검토결과, 압축강도 및 간이 수화열 실험 결과를 종합해 볼 때, Bottom Center의 경우 혼입비율 II(30:30:40), Roof의 경우 혼입비율 III(40:30:30)이 최적 혼입비율인 것으로 평가되었다.
The optimum binder ratio of the low heat mass concrete for LNG tank was evaluated in the present study. Three types of binder such as OPC I, ground granulated blast-furnace slag powder were mixed and were used. Also fine particle cement and activator were used to raise an early age strength development and ground limestone was used to reduce the cost. As a result of the study, mix ratio II (30:30:40) was suitable for Bottom Center and mix ratio III(40:30:30) was suitable for Roof based on compressive strength and semi-adiabatic temperature.