Ocean dumping of sewage sludge is banned. Therefore, it is needed to develop alternative treatment method. Sewage sludge and waste glass are used to prepare lightweight brick. Large amount of energy is consumed to prepare building material, because of its high preparation temperature, or above $1,200^{circ}C$. We study to prepare lightweight brick, using sewage sludge and waste glass as raw materials in this research. Lightweight brick was made at low temperature of below $800^{circ}C$ to reduce $CO_2$ emission by geopolymer technique. Calcination temperature, mixing ratio of sewage sludge/waste glass and water glass/water were discussed to evaluate their effect on the brick prepared. In this study, the optimal conditions for preparing bricks was $750^{circ}C$ of firing temperature, 1.5 of mixing ratio for water glass/water and 10 : 90 wt% of sewage sludge/waste glass. At this condition, compressive strength and specific gravity of brick prepared were 5.1 MPa and 0.46, respectively. These values satisfy the criteria on a lightweight brick.