IGZO thin films have been prepared by RF magnetron sputtering. The structural, electrical and optical properties of the IGZO thin films have been investigated as a function of deposition condition. XRD analysis of IGZO thin films showed a typical crystallographic orientation with c-axis perpendicular regardless of deposition conditions. The carrier mobility, carrier concentration and resistivity of the IGZO films sputtered at 200 W, 1mTorr and $300^{circ}C$ were $28.5cm^2/V{cdot}sec$, $2.6{ imes}10^{20}cm^3$, $8.8{ imes}10^{-4}{Omega}{cdot}cm$ respectively. The optical transmittance were higher than 80% at visible region regardless of the deposition conditions under the experiments above, and specifically higher than 90% at wave length over 500 nm. The absorption edge was shifted to shorter wavelength with increase of carrier concentration.