For the simplification of doping process in amorphous carbon film, arsenic (As) ions were implanted on the nucleated silicon wafer before the growth process. Then amorphous carbon films were grown at the condition of $CH_4/H_2=5%$ by microwave plasma chemical vapour deposition. Because the implanted seeds were grown at the high temperature and the implanted ions were spread, it was possible to reduce the process steps by leaving out the annealing process. When the implanted amorphous carbon films were electrically characterized in diode configuration, field emission current of $0.1mA/cm^2$ was obtained at the applied electric field of about $2.5V/{mu}m$. The results show that the implanted As ions were sufficiently doped by the self-annealing process by using the growth after implantation.