Tin and Tinoxide nanoparticles were prepared by arc-discharge nanopowder process. The negative electrode were fabricated using Tin and Tinoxide nanopower. The microstructure and electrochemistry properties were investigated and compared between Tin and Tinoxide. The oxidation film has microstructure of core/shell type and the shell which was attached around Tin nanoparticle consisted of amorphous $SnO_2$. The shape of Tinoxide nanoparticles was formed with irregular shape in comparison with Tin particle. Initial discharge capcity of Tinoxide electrode possesed about 1000mAh/g, which is about 320mAh/g higher than Tin electrode. Irreversible capacity of Tin electrode is much higher than Tinoxide. The cycle performance of Tinoxide electrode was indicated that is batter than Tin. The Tin negative electrode lost most of capacity after 4 cycle but Tinoxide electrode still retained the capacity. The Tinoxide does show some promise as Li-ion battery anode due to their large reversible capacity at low potentials.