Research and development of biodegradable bio-composite can replacement the synthetic polymer materials, which is used for automobile interior materials, finishing materials of air conditioner and refrigerator. To develop both components as biodegradable bio-composite, this research used natural polymer starch as matrix and kenaf fiber as a filler. Various plasticizer(polyvinyl alcohol, polyethylene glycol, glycerol) were added and examined the mechanical properties of the kenaf/starch bio-composites according to these plasticizer. The kenaf bast which cultivated in Korea was retted with 2 % NaOH solution. The plasticizer weighting 10 % of that of matrix was added. kenaf/starch composites were molded with hot press for 30 minutes at $130^{circ}C$ and 3,500 PSI molding condition. The mechanical properties such as tensile strength, elongation, and young modulus of the kenaf/starch composites were measured. Also, we measured the SEM cross-section images in order to investigate interfacial adhesion properties of fractured surfaces. The order of strength size of composites were G (12.42 MPa) > PVA (9.72 MPa) > PEG (4.73 MPa) samples respectively. The tensile strength of PEG sample is lower than the control sample (5.40 MPa).