Effect of multi-stacked layer (MSL), 0.1 mol (M) and 0.3 mol (M) hafnium oxide ($HfO_2$) alignment layers were fabricated via a solution-process for LCs orientation. The solutions were spin-coated and annealed in a furnace. MSL consists of three sub-layers using 0.1 M solution, mono-layer (ML) is composed of 0.3 M $HfO_2$ solution. Then ion-beam irradiation was treated with 1.8 keV for 2 min. $HfO_2$-based LC cells were investigated through photographs, pre-tilt angle using crystal rotation method, X-ray photoelectron spectroscopy (XPS) measurement, and surface roughness using atomic force microscopy(AFM) for their characteristic research. Good LC orientation characteristics were observed on MSL $HfO_2$ surface. The LC alignment mechanism on MSL $HfO_2$ and ML $HfO_2$ surfaces was attributed to van der Waals (VDW) interaction between the LC molecular and substrate surface.