Generation rate of construction wastes in Korea has occupied preponderantly in recent years. To understand chemical properties of recycled concrete aggregate (RCA), RCA samples were tested for their leaching characteristics. Leaching tests were conducted according to Korean Standard Leaching Test (KLT) and Toxicity Characteristics Leaching Procedure (TCLP) respectively. The RCA samples were characterized using X-ray fluorescence (XRF). Alkalinity of the leachate was determined using a pH meter titration method. The XRF analysis result shows that the calcium oxide (CaO) content in the RCA sample is 25.3~50.4 %. When the RCA sample was mixed with water in a batch reactor, pH in the solution was rapidly increased, and 70% of the total pH change was found in 1 hour. The TCLP showed slightly higher efficiency for leaching heavy metals than the KLT. The leaching efficiency was also higher as the particle size of RCA sample was smaller. The leaching test results suggest that RCA can be generally classified as nonhazardous waste.