We grew the $Li_6Gd(BO_3)_3:Ce^{3+}$ scintillator and determined the scintillation and thermoluminescence properties for X-rays. The emission spectrum of $Li_6Gd(BO_3)_3:Ce^{3+}$ is located in the range of 370~500 nm, peaking at 423 nm an 455 nm, due to the $4f{ ightarrow}5d$ transition of $Ce^{3+}$ ions. The fluorescence decay time of the crystal is composed three components. The fast component is 60 ns (25%), the intermediate component is 787 ns (29%) and the slow component is $5.9{mu}s$ (46%) of the crystal. The after-glow is caused by the electron and hole traps in the crystal lattice. We determined physical parameters of the traps in the crystal. The thermoluminescence trap are composed two traps. The determined activation energy (E), kinetic order (m) and frequency factor (s) of the first trap are 0.65 eV, 1.01 and $6.9{ imes}10^8s^{-1}$. And, the determined activation energy, kinetic order and frequency factor of the second trap are 0.96 eV, 1.79 and $3.1{ imes}10^{12 }s^{-1}$, respectively.