This article describes effect of post heat treatment on wear characteristics of thermally sprayed Co-based self-flux alloy coating. Co-based self-flux alloy coatings were deposited on steel substrates using a flame spray process. Post heat treatments were carried out at 800, 900, 1000 and $1100^{circ}C$ for 30min in a vacuum chamber. For analysis of effect of post heat treatment on mechanical properties, wear test and hardness test were performed for post heat-treated coating specimen. Microstructures of heat treated coating layer and wear track were examined using SEM and EDS. Wear loss and hardness became lower with increasing post heat treatment temperature.