The samples of $Ba_2CoZnFe_{12}O_{22}$ was synthesized by the solid-state reaction method. The toroids of $Ba_2CoZnFe_{12}O_{22}$ were sintered with various sintering temperature at 1050, 1100, 1150, and $1200^{circ}C$, and studied by x-ray diffractometer, vibrating sample magnetometer, network analyzer, and Mssbauer spectrometer. From the XRD patterns, the density of samples increased with increasing sintering temperature. From the magnetic hysteresis curves up to 10 kOe at 295 K, the saturation magnetization ($M_s$) of $Ba_2CoZnFe_{12}O_{22}$ samples in various sintered at 1050, 1100, 1150 ,and $1200^{circ}C$ were showed around $M_s$= 33.0 emu/g. However, With increasing sintering temperature, the coercivity ($H_c$) of samples decrease. Complex permeability and permittivity of samples in various sintering temperatures were measured between 100MHz to 4 GHz. With increasing sintering temperature, the permeability of samples increase.