This study investigates the preparation of anti-reflective (AR) coating film to improve the efficiency of solar cell. The AR coating film was successfully obtained by dip-coating with AR coatings prepared by sol-gel method. Fluoroalkylsilane was additionally introduced into the coatings to give the self-cleaning effect of AR coating film. We performed the abrasion test, pencil scratch hardness test and cross-cut test to identify the mechanical strength of AR coating film. As the results, the transmittance of AR coating films with 9.07, 18.13 and 27.20 of IPA/MTMS molar ratios were 93.1, 93.6 and 95.3%, respectively. The water contact angle and transmittance of AR coating film increased by the introduction of hydrophobicity. The prepared AR coating film shows the high level of abrasion, hardness and adhesion. The IPA/MTMS molar ratio of 27.20 and the withdrawing speed range of 0.20 ~ 0.28cm/sec are the optimal coating condition in terms of the transmittance and mechanical strength of AR coating film.