PURPOSES : The objective of this study is to investigate the effect of asphalt and geotextile interlayer on the fracture behavior of unbonded concrete overlay through a laboratory composite beam test. METHODS : In order to evaluate the effect of interlayer materials on the fracture behavior of unbonded concrete overlay, a laboratory test of composite beam was conducted with different types of interlayer. The test results of the composite beam using two types of geotextile interlayer with different thicknesses were compared to the test results of the composite beam using the tradition type of asphalt interlayer. The unbonded concrete overlay on the existing concrete pavement without interlayer was set for the control condition. RESULTS AND CONCLUSION : Overall, the laboratory composite beam test results did show the effect of asphalt and geotextile interlayer on the fracture behavior of composite concrete beams. The three-layer geotextile interlayer and HMA layer both increase the peak load when the first macrocrack occurs in the top concrete beam, while the HMA interlayer causes the smallest load drop percentage after the first macrocrack. The three-layer geotextile did show better performance than the single-layer geotextile through the greater peak load and smaller load drop percentage. It indicates that the thickness of geotextile interlayer will affect the fracture behavior of unbonded concrete overlay and the thicker geotextile interlayer is recommended.