This is the study on diffusion of ceramic body oxide compounds to glaze. For ceramic bodies, no ferrous oxides contain white ware, celadon, and 3 wt% iron oxides contained white ware was used in this experiment. These ceramic bodies were glazed by transparency glaze, iron oxides contained glaze, and glaze made by pine tree ash that treated in 1240 degree, under reduction condition for an hour. An electron probe microanalyzer(EPMA) was used to study diffusion of oxides and to calculate distance of ceramics bodies. As a result, only iron oxide and magnesium oxide from the body diffused to glaze, and also made a band which shown very thin layer of iron oxide and magnesium oxide between the body and glaze. The densest band of iron oxide formed 100 to $150{mu}m$ in the glaze, and the densest band of magnesium oxide was found 50 to $100{mu}m$ in the glaze. Therefore, it could be concluded that iron oxide in the body is diffused to the glaze and it affects the color of glaze, even though iron oxide exists in the glaze. Furthermore, the thickness of the glaze has an effect on the color of celadon.