Thin films of cubic $Na_{0.6}WO_3$, which is one of the sodium tungsten bronze, were fabricated by rf sputtering for the electrode applications in integrated sensors and actuators. A single-phase cubic $Na_{0.6}WO_3$ sputtering target of power type was prepared by conventional solid-state reaction. Thin films were deposited from the powder target, and the as-deposited films were amorphous, thus they annealed by tube furnace or RTP for crystallization. Thin films having cubic phase $Na_xWO_3$ were fabricated by the optimization of sputtering and post-annealing conditions, but single-phase cubic $Na_{0.6}WO_3$ thin films were not obtained. Although the films were not in single phase, they had good electrical conduction properties showing electrical resistivities of $10-4{Omega}{cdot}cm$ order.