Swelling of the heat-treated netting for gillnet was estimated through the netting height in square acrylic tank. Experimental Nylon netting and PBSAT netting were heat-treated by using the high-degree vacuum method in hot water after net making. Heat-treatment temperatures were conducted with Nylon netting $105^{circ}C$ and PBSAT netting $62^{circ}C$, $65^{circ}C$, $66^{circ}C$, $67^{circ}C$. The swelling measurement method of a netting using the square tank was capable of the reduction measurement errors comparing with measurement methods of a mesh inner angle and the shortening rate of a mesh size. In addition, this method was available to comparison evaluation for each netting more easily. Wet type heat-treatment apparatus with high-degree vacuum was shown higher $7{sim}8^{circ}C$ inner side temperature than a setting temperature. The tensile strength and elongation of Nylon netting and PBSAT netting were shown higher wet condition than dry condition. The tensile strengths of PBSAT monofilaments in dry and wet condition were sharply decreased at heat-treatment temp. $75^{circ}C$ than heat-treatment temp. $74^{circ}C$.