The surface of an ordered mesoporous silica (OMS) was functionalized using 1H,1H,2H,2H-perfluorooctyltrimethoxysilane at $20^{circ}C$ and $60^{circ}C$. It was shown that only elevated temperature allows lyophobic properties on the walls of OMS, eventually preventing pore flooding with nonaqueous electrolytes. The functionalized OMSs (OMS-F) were characterized with various techniques: wettability test, $N_2$ sorption measurement, high-resolution transmission electron microscopy (HR-TEM). Cathodes of $10mg/cm^2$ loading were prepared with a commercial Pt/C catalyst and polyvinylidene fluoride (PVDF, 2.5 wt.%) binder using a typical doctor blade method on a commercial gas diffusion layer (GDL) in the presence or in the absence of OMS-F additives. Subsequent discharge-charge curves were taken in a 1M LiTFSI-TEGDME electrolyte at 60oC in pure oxygen atmosphere. It was found that the discharge capacity was significantly affected by OMS-F: 5 wt.% of additive extended discharge capacity by a factor 1.5. On the other hand, a similar OMS material but synthesized at $20^{circ}C$ did not show lyophobic properties and deteriorated cathode capacity.