This study was performed to test combustive properties of medium density fibreboard (MDF) plates treated with piperazinomethyl-bis-phosphonic acid (PIPEABP), methylpiperazinomethyl-bis-phosphonic acid (MPIPEABP), and N,N-dimethylethylenediaminomethyl-bis-phosphonic acid (MDEDAP). MDF specimens were painted three times with 15 wt% solution of the alkylenediaminoalkyl-bis-phosphonic acids at room temperature. After drying specimen treated with chemicals, combustive properties were examined using the cone calorimeter (ISO 5660-1). As a result, combustion-retardation properties increased due to the treatment of bare MDF with alkylenediaminoalkyl-bis-phosphonic acid solution. Especially, the specimens treated with chemicals showed the ignition (TTI) (148 s~116 s) was retarded and the flameout (Tf) (633 s~529 s) time increased, while the total heat release rate (THRR) (61.1~67.0) $MJ/m^2$ was lowered than those of using virgin plate by reducing the burnig rate. Compared with virgin MDF plate, the specimens treated with the alkylenediaminoalkyl-bis-phosphonic acids showed low combustive properties. However the specimens treated with bis-(dimethylaminomethyl) phosphinic acid (DMDP) showed the higher peak heat release rate (PHRR) ($185.08kW/m^2$) than that of the virgin plate.