An investigation of the influence of $WO_3$ addition with different precursors and preparation methods on the phase formation and selective catalytic reduction (SCR) efficiency of anatase-$TiO_2$ powders has been carried out. An anatase-$TiO_2$ synthesized by precipitation process was used as a catalyst support. For $WO_3(10wt%)/TiO_2$, the W loading to the $TiO_2$ support led to the lower in anatase to rutile transition temperature to ${sim}900^{circ}C$ from $1200^{circ}C$ of the $TiO_2$ support alone. In the case of $WO_3(10wt%)/TiO_2$ SCR powders obtained from a wet process with ammonium meta-tungstate (AMT) precursor, the highest $NO_X$ conversion efficiency was achieved at $450^{circ}C$ remaining high efficiency at $500^{circ}C$, while the same composition prepared from a dry process with $WO_3$ addition showed the lowered efficiency with temperature after reaching the efficiency maximum at $350^{circ}C$. The same tendency has been found that the $V_2O_5(5wt%)-WO_3(10wt%)/TiO_2$ SCR powders obtained from the wet process with AMT precursor has shown the superior $NO_X$ conversion efficiency over 90 % in a wider temperature range of $300{sim}500^{circ}C$.